Welding repairing characteristics and process of ASME SA572 Grade 50 low alloy steel plates steel plate

Because of the different kinds of alloy elements and the alloy content, the difference of welding performance between ASME SA572 Grade 50 low Alloy steel plates and alloy steel plates is remarkable. Under normal circumstances, the mass fraction of ASME SA572 Grade 50 low alloy steel plates carbon is below 0.4%, and the welding performance is still very good. And the alloy steel with yield strength higher than 400MPa has a mass fraction of 0.4%, which is very hardened and easy to generate cold cracks.

ASME SA572 Grade 50 low alloy steel plates welding technology:
1. In general, ASME SA572 Grade 50 low alloy steel plates preheating is needed before welding, and the preheating temperature is 100-150℃.

2. To control the cooling speed strictly. The welding current can be increased and the welding speed can be slowed down in order to slow cooling.

3. The low hydrogen welding rod with strong crack resistance should be used as far as possible.

4. Heat treatment after welding is used to prevent cold crack.

BBN steel is engaged in ASME SA572 Grade 50 low alloy steel plates supply and technology development. We have make breakthrough year by year, becoming leading ASME SA572 Grade 50 low alloy steel plates supplier and exporter in China. We are open and welcome cooperation from each corner of the world.

Share
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Spot Resource