C55R steel

C55R EN 10083-2:2002, Number: 1.1209

Comparison of steel grades

JUS

Č.1680

DIN

(C55R, Cm55)

BS

(070M55)

GOST

55

AISI

(1055)

UNI

-

NF

(XC55H1)

C55R Chemical analysis -% by mass

Chemical elements

C

Si max.

Mn

P max.

S1 max.

Cr max.

Mo max.

Ni max.

Cr+Mo+Ni max.

%, by mass

0,52-0,60

0,40

0,60-0,90

0.025

0,035

0,40

0,10

0,40

0,63

Permissible deviation

± 0.02

+0,03

± 0,04

+ 0.005

+ 0.005

+0,05

+0,03

+0,05

-

Jominy’s hardenability band

Distance in mm from quenched end Hardness in HRC

Symbol

mm

1

2

3

4

5

6

7

8

9

10

11

13

15

20

25

30

+H

max.

65

64

63

62

60

57

52

45

37

36

35

34

33

32

30

29

min.

58

55

47

37

33

32

31

30

29

28

27

26

25

24

22

20

Tentative values for the ’’C’’ scale Rockwell hardness for special steel grades with restricted hardenability scatter bands (+HH and +Hl grades)

Symbol

Distance in mm from the quenched end HRC hardness

1

4

5

+HH5 +HH15 +HL5 +HL15

-

-

42 to 60

60 to 65

-

42 to 60

-

-

33 to 51

58 to 63

-

33 to 51

Maximum hardness for products to be supplied in the ’’treated to improve shearability (+S)’’ or ’’soft annealed (+A)’’ condition

+S (HB max.)

+A (HB max.)

255

229

C55R Mechanical properties in the quenched and tempered condition (+QT)

 

Mechanical properties for the ruling sections (see prEN10083-1:2002, Annex A) with a diameter (d) or for flat products trickness (t) of

d ≤ 16mm t ≤ 8mm

16mm < d ≤ 40mm 8mm < t ≤ 20mm

40mm < d ≤ 100mm 20mm < t ≤ 60mm

Re min (MPa)

550

490

420

Rm (MPa)

800-950

750-900

700-850

A min. (%)

12

14

15

Z min. (%)

30

35

40

KV min. (J)

-

-

-

C55R Mechanical properties in the normalized condition – (+N)

 

Mechanical properties for products with a diameter (d) or, for flat products trickness (t) of

d ≤ 16mm t ≤ 16mm

16mm < d ≤ 100mm 16mm < t ≤ 100mm

100mm < d ≤ 250mm 100mm < t ≤ 250mm

Re min. (MPa)

370

330

300

Rm min. (MPa)

680

640

620

A min. (%)

11

12

12

Hardness of surface hardened zones for special steels intended for flame and induction hardening

HRC min. 58

C55R Heat treatment conditions

Quenching 0C

Quenching agent

Tempering temperature 0C

Hardening temperature in the end quench test 0C

Normalizing 0C

805-840

Oil or water

550-660

8300±5

825 to 885


Bebon International is a professional C55R steel exporter and a steel Stockist in china. We keep more than 1000 tons C55R steel in stock every month. If you want to get the C55R steel price, please do not hesitate to contact us. Any need in C55R Chemical Composition and Mechanical Properties, please feel free to contact us by email or calling to us.
Share
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Spot Resource