Home > Sellinglist - NM400 vs AR400

NM400 vs AR400 steel plate

NM400 and AR400 are both types of wear-resistant steel, but they come from different standards and have specific properties tailored for various applications. Here's a detailed comparison:

NM400

Specifications:

Standard: Chinese GB/T 24186

Hardness: 360-440 HBW

Yield Strength: ≥ 800 MPa

Tensile Strength: ≥ 1250 MPa

Elongation: ≥ 10%

Impact Toughness: Good impact toughness, especially at lower temperatures

Applications:

Used in the manufacturing of mining machinery, construction machinery, and parts for industrial equipment.

Suitable for applications requiring resistance to abrasion and moderate impact.

AR400

Specifications:

Standard: ASTM (American Society for Testing and Materials)

Hardness: 360-440 HBW

Yield Strength: ≥ 1000 MPa

Tensile Strength: 1400 MPa

Elongation: 10-15%

Impact Toughness: Generally good, but can vary based on the specific manufacturer and batch.

Applications:

Commonly used in the manufacturing of conveyors, truck beds, chutes, and other equipment subjected to wear and tear.

Ideal for applications that require a balance between hardness and formability.

Key Differences

Standards:

NM400: Follows the Chinese GB/T 24186 standard.

AR400: Follows the ASTM standard commonly used in the United States.

Chemical Composition:

The exact chemical composition can vary between manufacturers, but generally, NM400 may have slightly different alloying elements compared to AR400, leading to variations in specific properties.

Mechanical Properties:

Yield Strength: AR400 typically has a higher yield strength compared to NM400.

Tensile Strength: AR400 usually has a higher tensile strength.

Hardness: Both steels have similar hardness levels, typically around 400 HBW.

Applications:

NM400: Often used in industries within China and other regions following Chinese standards, especially where a balance of hardness and toughness is required.

AR400: Widely used in North America and other regions following ASTM standards, particularly in applications requiring a tough, durable wear-resistant steel.

Summary

Both NM400 and AR400 are high-strength, wear-resistant steels with similar hardness levels, but they adhere to different standards and exhibit slight differences in mechanical properties. The choice between NM400 and AR400 depends largely on the specific requirements of the application and the regional standards being followed.

Share
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Spot Resource