JIS G 3132 SPHT-2 steel is a material grade and designation defined in JIS G 3132 standard. JIS G 3132 is a Japanese material standard for Hot rolled steel plates, sheets, strips for pipes & tubes making.
JIS G 3132 SPHT-2 steel is a Hot Rolled steel in the form of plates, sheets & strips for pipes & tubes making. This quality of hot Rolled steel is a type of steel that is utilized in making pipes & tubes material. A comparison with SPHT-1 steel will show how SPHT-2 steel differs with lowered tensile strength steel of the same category.
Dimensional Characteristics of SPHT-2 Steels: The applicable thickness for this SPHT-2 material as defined in the JIS 3132 starts from 1.2 mm to 14 mm. However the width of SPHT-2 material ranges to 950 to 2000 mm.
JIS G 3132 SPHT-2 steel Chemical Composition:
JIS G 3132 defines the chemical composition of SPHT-2 steels as under:
Maximum percentage of Carbon (C) is 0.18 percent.
Maximum percentage of Manganese (Mn) is 0.60 percent.
Maximum percentage of Silicon (Si) is 0.35 percent.
Maximum percentage of Phosphorous (P) is 0.040 percent.
Maximum percentage of Sulphur (S) is 0.040 percent.
Remaining is iron (Fe) percentage and with few negligible impurities.
JIS G 3132 SPHT-2 steel Mechanical Properties:
The tensile strength of the SPHT-2 Steels is expressed in Newton per millimeters and it must be at-least 340 N/mm2 (MPa). The elongation property of SPHT-2 steel varies with the ranges of thickness. The minimum percentage ranges for elongation is 25 minimum.
JIS G 3132 SPHT-2 steel Applications : SPHT-2 steel is used for pipes & tubes making.