C40R EN 10083-2:2002, Number: 1.1189 |
Comparison of steel grades |
|
JUS |
Č.14343 |
|
DIN |
Ck40 |
|
BS |
(080M40) |
|
GOST |
40 |
|
AISI |
1040 |
|
UNI |
- |
|
NF |
(XC42H1), XC38 |
C40R Chemical analysis-% by mass
Chemical elements |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Ni |
Cr+Mo+Ni |
%,by mass |
0,37-0,44 |
0,40 |
0,50-0,80 |
0.025 |
0,020-0,040 |
0,40 |
0,10 |
0,40 |
0,63 |
Permissible deviation |
± 0.02 |
+0,03 |
± 0,04 |
+ 0.005 |
± 0.005 |
+0,05 |
+0,03 |
+0,05 |
- |
Jominy’s hardenability band
Distance in mm from quenched end Hardness in HRC (mm) | |||||||||||||||||||
Symbol |
mm→ |
1 |
2 |
3 |
4 |
5 |
6 |
7 |
8 |
9 |
10 |
11 |
13 |
15 |
20 |
25 |
30 |
||
+H |
max. |
60 |
60 |
59 |
57 |
53 |
47 |
39 |
34 |
31 |
30 |
29 |
28 |
27 |
26 |
25 |
24 |
||
min. |
51 |
46 |
35 |
27 |
25 |
24 |
23 |
22 |
21 |
20 |
- |
- |
- |
- |
- |
Tentative values for the ’’C’’ scale Rockwell hardness for special steel grades with restricted
hardenability scatter bands (+HH and +Hl grades)
Symbol |
Distance in mm from the quenched end HRC hardness |
||
1 |
4 |
5 |
|
+HH4 |
- |
38 to 57 |
- |
54 to 60 |
38 to 57 |
- |
|
- |
27 to 46 |
- |
|
51 to 57 |
27 to 46 |
- |
Maximum hardness for products to be supplied in the ’’treated to improve shearability (+S)’’ or
’’soft annealed (+A)’’ condition
+S (HB max.) |
+A (HB max.) |
- |
- |
Mechanical properties in the quenched and tempered condition (+QT) )
Mechanical properties for the ruling sections (see prEN10083-1:2002, Annex A) with a diameter (d) or for flat products trickness (t) of |
|||
d ≤ 16mm t ≤ 8mm |
16mm < d ≤ 40mm |
40mm < d ≤ 100mm |
|
Re min (MPa) |
460 |
400 |
350 |
Rm (MPa) |
650-800 |
630-780 |
600-750 |
A min. (%) |
16 |
18 |
19 |
Z min. (%) |
35 |
40 |
45 |
KV min. (J) |
30 |
30 |
30 |
C40R Mechanical properties in the normalized condition – (+N)
Mechanical properties for products with a diameter (d) or, for flat products trickness (t) of |
|||
d ≤ 16mm t ≤ 16mm |
16mm < d ≤ 100mm |
100mm < d ≤ 250mm |
|
Re min. (MPa) |
320 |
290 |
260 |
Rm min. (MPa) |
580 |
550 |
530 |
A min. (%) |
16 |
17 |
17 |
C40R Heat treatment conditions
Quenching, 0C |
Quenching agent |
Tempering temperature, 0C |
Hardening temperature in the end quench test,0C |
Normalizing, 0C |
830-870 |
Water or oil |
550-660 |
8700±5 |
850 to 910 |