ASTM A283 Grade D steel,ASTM A283 Intermediate Strength Hot Rolled Grade D Steel steel plate

ASTM A283 Grade D steel is a low & intermediate tensile strength hot rolled steel in the form of plates for general Intermediate Strength applications. Grade D is a material Grade and designation defined in ASTM A283 standard. ASTM A283 is an American material standard for Hot rolled steel plates for general intermediate strength usage. Grade D steel is relatively higher in strength than Grade C steel of the same standard.

ASTM A283 Grade D steel Dimensional Characteristics: The applicable thickness for this Grade D material as defined in the ASTM A283 starts from 6 mm to 50 mm. The width is normally from 600 mm to 2000 mm.

ASTM A283 Grade D steel Chemical Composition: ASTM A283 defines the chemical composition of Grade D steels as under:

Maximum percentage of Carbon (C) is 0.27

Maximum percentage of Silicon (Si) is 0.4

Maximum percentage of Manganese (Mn) is 0.9

Maximum percentage of Phosphorous (P) is 0.035

Maximum percentage of Sulphur (S) is 0.040

Minimum percentage of Copper (Cu) is 0.20

Remaining is iron (Fe) percentage and with few negligible impurities.

ASTM A283 Grade D steel Mechanical Propertie: The tensile strength of the Grade D Steels is expressed in Newton per millimeters and it must be at-least 415 N/mm2 (MPa). The yield strength is minimum 230 N/mm2 (MPa). The minimum percentage ranges for elongation is 23%.

As a ASTM A283 Grade D steel supplier in China, any need in ASTM A283 Grade D steel,pls contact us!

Share
Are you also interested in further steel processing (machining)?

Just like you, 70% customers choose long-term cooperation with BBN steel not only for our good product and service quality, good reputation in the international market, but also for our experienced one-stop raw material supply and further steel processing!

Fabrication and Machining Service24h Technical support

Spot Resource