Home > Steel plate > ASME - ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate

ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate steel plate

ASME SA514/ SA514M Grade E quenched and tempered alloy steel plates are high yield strength steel of structural quality in thickness of 150mm and under intended primarily for use in welded bridges and other structures. ASME SA514/ SA514M Grade E quenched and tempered alloy steel plates are mainly used to make mechanical device and other structural elements and so on drilling machine, power shovel, electricity drive wheel counter- mine trolley, mineral product automobile, car loader, etc.

ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate chemical composition:

Grade C Mn P S SI Ni Cr Mo V Ti Zr Cu B
SA514 Gr.E 0.12-0.20 0.40-0.70 ≤0.035 ≤0.04 0.20-0.35 ~ 1.40-2.00 0.40-0.60 ~ 0.04-0.10 ~ 0.20-0.40 0.0015-0.005

ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate mechanical property:

Grade Thickness
Inch
Yield Strength
Mpa
Tensile
Strength
Mpa
Elongation in 50mm Hardnees
Brinell
SA514 Gr.E less 3/4 inch 690 760-895 18 235
over 3/4 to 2 1/2 690 760-895 18 ~
over 2 1/2 to 6 inch 620 690-895 16 ~

ASME SA514/ SA514M Grade E quenched and tempered alloy steel plates shall be heat treated by the mill to conform to the tensile and hardness requirements by heating to not less 900 degree for quenching in water or oil, and tempering at not less 620 degree.


Bebon International is a professional ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate steel exporter and a steel Stockist in china. We keep more than 1000 tons ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate steel in stock every month. If you want to get the ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate steel price, please do not hesitate to contact us. Any need in ASME SA514/ SA514M Grade E quenched and tempered alloy steel plate Chemical Composition and Mechanical Properties, please feel free to contact us by email or calling to us.